Synthesis and characterization of new pyrochlore solid solution Bi1.5Sb1.5–xNbxCuO7 - 25/07/14
pages | 6 |
Iconographies | 6 |
Vidéos | 0 |
Autres | 0 |
Abstract |
New pyrochlore solid solutions Bi1.5Sb1.5–xNbxCuO7 have been synthesized (0≤x≤1.5) via the ceramic method in the air at 1000°C. Rietveld refinement of the compounds Bi1.5Sb1.5–xNbxCuO7 for x=0, x=0.75 and x=1.5 by means of X-ray powder diffraction analysis confirmed an overall A2B2O7 cubic pyrochlore structure according to (Bi3+1.5Cu2+0.5)(Sb5+1.5–xNb5+xCu2+0.5)O7 formula with 10.42009 (3)Å, 10.47193 (3)Å and 10.52679(4)Å, respectively, and space group. Composition dependencies of cell parameters show a linear increase with the niobium x fraction. The magnetic susceptibility measurements achieved between 4 and 400K indicate a paramagnetic behavior with an oxidation state “+2” for the copper ion. The electric resistivity measured using complex impedance spectroscopy evidences an increase of the electric conductivity with temperature and niobium substitution.
Le texte complet de cet article est disponible en PDF.Keywords : Pyrochlore, Oxides, Synthesis, Solid solutions
Plan
Vol 17 - N° 9
P. 899-904 - septembre 2014 Retour au numéroBienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?