Failure locus of polypropylene nonwoven fabrics under in-plane biaxial deformation - 10/05/12
, Carlos González a, b , Javier Llorca a, b, ⁎ Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
| pages | 13 |
| Iconographies | 0 |
| Vidéos | 0 |
| Autres | 0 |
Abstract |
The failure locus, the characteristics of the stress–strain curve and the damage localization patterns were analyzed in a polypropylene nonwoven fabric under in-plane biaxial deformation. The analysis was carried out by means of a homogenization model developed within the context of the finite element method. It provides the constitutive response for a mesodomain of the fabric corresponding to the area associated to a finite element and takes into account the main deformation and damage mechanisms experimentally observed. It was found that the failure locus in the stress space was accurately predicted by the Von Mises criterion and failure took place by the localization of damage into a crack perpendicular to the main loading axis.
Le texte complet de cet article est disponible en PDF.Keywords : Nonwoven fabric, In-plane biaxial deformation, Failure locus, Finite element method
Plan
Vol 340 - N° 4-5
P. 307-319 - avril 2012 Retour au numéro
Article précédent
- Effective elastic properties of nanocomposites using a novel atomistic–continuum interphase model
- Bhasker Paliwal, Mohammed Cherkaoui, Omar Fassi-Fehri
- Homogenization of cellular sandwich panels
- Arthur Lebée, Karam Sab
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?