Anchorage miniscrews: A surface characterization study using optical microscopy - 20/09/11
pages | 14 |
Iconographies | 8 |
Vidéos | 0 |
Autres | 0 |
Summary |
Introduction |
The aim of this study was to assess the surface changes in orthodontic miniscrew implants retrieved after usage and compare them with brand-new, as-received control miniscrews.
Material and methods |
The study sample consisted of 28 miniscrews from the same manufacturer: Dual Top Anchor system® (Korea) of different diameters and lengths. One brand-new miniscrew served as a control. Surface characterization was carried out using optical microscopy (Leica DM2500M®) and image magnification (×5, ×10 and ×20).
Results |
Observations under optical microscopy showed signs of pitting and crevice corrosion mainly at manufacturing defects. Retrieved miniscrew implants displayed larger surface cracks from corrosive attacks (pitting and crevice). Qualitative sample analysis suggested a loss of gloss and texture, giving the surface a dull appearance. Localized pitting was the most frequent form of corrosion observed in our sample.
Discussion and conclusion |
Despite a smooth appearance to the naked eye, the miniscrews all had crack-like surface manufacturing defects. Examination of the surface of these miniscrews, after usage, evidenced pitting or crevice corrosion principally in the area of enhance corrosion resistance.
Le texte complet de cet article est disponible en PDF.Key-words : Miniscrews, Surface characterization, Titanium, Corrosion
Plan
Vol 9 - N° 3
P. 325-338 - septembre 2011 Retour au numéroBienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?