Effect of eliminating the residual fluoride gel on titanium bracket corrosion - 20/09/11
pages | 18 |
Iconographies | 7 |
Vidéos | 0 |
Autres | 0 |
Summary |
Introduction |
Fluoride ions, in long-term applications on titanium brackets, cause their corrosion. Fluoride gel used for caries prevention during orthodontic treatment has a very high concentration in fluoride ions, and therefore has the potential for causing bracket corrosion. The main aim of this study was to determine the effect of eliminating the residual fluoride gel, by rinsing it, on the corrosion of titanium brackets. The secondary aim was to evaluate the corrosion of titanium brackets in the presence of fluoride gel.
Methods |
One hundred titanium brackets were divided into five groups of 20 brackets each. Group 1 being the control group, the rest of the groups were immersed in fluoride gel: Group 2 for 4minutes and kept for 30minutes with the residual fluoride gel on; Group 3 for 4minutes followed by immediate water rinsing; Group 4 for 12minutes and kept for 90minutes with the residual fluoride gel on and Group 5 for 12minutes followed by immediate water rinsing. All groups were rinsed then dried, for 20hours, using Silica gel in a desiccator maintained at 37°C before testing.
Results |
Gravimetrical results and SEM analysis showed no significant difference between Groups 2, 3 and 5 compared to each other and to the control group. Only Group 4 showed significant weight loss and pitting corrosion in four of the 20 brackets. In sliding resistance, no significant difference was detected between any of the groups.
Conclusions |
Short time applications of fluoride gel do not affect sliding resistance of titanium brackets. No titanium corrosion was detected for one application of concentrated fluoride gel and some brackets showed pitting corrosion for three applications. The rinsing of residual fluoride gel eliminates completely the risk of bracket corrosion.
Le texte complet de cet article est disponible en PDF.Key-words : Titanium brackets, Fluoride gel, Corrosion
Plan
Vol 9 - N° 3
P. 298-315 - septembre 2011 Retour au numéroBienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?