Nickel–manganese mixed oxides were prepared with sol–gel and coprecipitation methods. The characterization of the different samples was made by XRD, TPR, FT-IR and Raman spectroscopies. NiMn₂O₄ spinel was obtained at a calcination temperature of 900°C; the solids calcined at 750°C give in addition to the spinel phase, an ilmenite phase (NiMnO₃) and a Mn₂O₃ phase. Preliminary reactivity results of partial oxidation of methane on NiMn₂O₄ and sub-stoichiometric Ni_xMn_3−xO₄ are given. The catalysts calcined at 900°C presented the best methane conversion at 700°C. The solid containing the ilmenite phase leads to a high CO₂ selectivity revealing a good activity towards the complete oxidation of methane.

Les oxydes mixtes nickel–manganese ont été préparés par deux méthodes différentes : coprécipitation et la méthode sol–gel. Les différents solides préparés ont été caractérisés par DRX, TPR, FT-IR et spectroscopie Raman. Une structure spinelle pure a été obtenue après calcination à 900°C; les solides calcinés à 750°C donnent lieu, en plus de la phase spinelle, à deux phases supplémentaires NiMnO₃ et Mn₂O₃. NiMn₂O₄ et les solides sous-stoechiométriques Ni_xMn_3−xO₄ ont été testés dans la réaction d’oxydation partielle du méthane. Les catalyseurs calcinés à 900°C conduisent à la meilleure conversion du méthane. Une sélectivité importante en CO₂ a été obtenue avec le solide contenant la phase ilménite révélant ainsi une bonne activité dans la réaction d’oxydation complète du méthane.