Structure and properties of glasses in the system Li2O-SnO-B2O3 - 04/04/08
![](/templates/common/images/mail.png)
pages | 7 |
Iconographies | 9 |
Vidéos | 0 |
Autres | 0 |
Abstract |
Glasses in the system Li2O-SnO-B2O3 system were prepared by a melt-quenching method. Thermal and viscous properties and local structure of these glasses were investigated. The SnO-B2O3 glasses exhibited relatively low glass-transition temperatures (Tg) around 350 °C and excellent thermal stability against crystallization. Viscosity measurements in the vicinity of Tg indicated that the glasses were considerably fragile compared to alkali borate glasses. Fraction of four-coordinated boron was maximized at the composition with 50 mol% SnO and that of nonbridging oxygen, which is not purely ionic in alkali borate systems but partially covalent, augmented with an increase in the SnO content. Correlation between glass properties and structure was discussed in the SnO-B2O3 binary system.
Le texte complet de cet article est disponible en PDF.Résumé |
Des verres de borates d'étain et de lithium ont été étudiés du point de vue des structures locales, viscosité et propriétés thermiques, révélant que ces verres sont fragiles. Les relations entre propriétés et structures sont discutées.
Le texte complet de cet article est disponible en PDF.Keywords : borate glass, SnO based glass, glass-transition temperature, viscosity, glass structure, NMR, XPS
Mots-clé : verres de borate, structure, propriétés thermiques
Plan
Vol 5 - N° 11
P. 751-757 - novembre 2002 Retour au numéroBienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?