Effect of the defect initial shape on the fatigue lifetime of a continuous casting machine roll - 09/07/16
, Yuri Lapusta bBienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
| pages | 7 |
| Iconographies | 7 |
| Vidéos | 0 |
| Autres | 0 |
Abstract |
The article deals with the influence of the defect initial shape on the residual lifetime of a continuous casting machine roll made of 25Cr1MoV steel. Based on this approach, previously proposed by some authors, the growth of the surface fatigue crack was modeled in a roll under loading and temperature conditions that are close to operational ones, taking into account the statistical distribution of the C parameter of Paris' equation. Dependencies of the continuous casting machines roll fatigue lifetime on the initial defect shape and critical defect sizes are obtained.
Le texte complet de cet article est disponible en PDF.Keywords : Fatigue, 25Cr1MoV steel, Continuous casting machine roll, Stress intensity factor, Semi-elliptical surface crack, Lifetime
Plan
Vol 344 - N° 8
P. 596-602 - août 2016 Retour au numéro
Article précédent
- Equivalent Liénard-type models for a fluid transmission line
- Lizeth Torres, Jorge Alejandro Delgado Aguiñaga, Gildas Besançon, Cristina Verde, Ofelia Begovich
- Effect of temperature on the time-dependent behavior of geomaterials
- Sheng Zhang, Shuo Xu, Jidong Teng, Yonglin Xiong
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?