This paper summarizes the results of a research on the influence of the poisoning of the SCR catalyst on its structure. Samples of commercially available SCR catalysts were exposed to real flue gases inside a pulverized coal boiler co-firing coal and biomass. The catalysts were investigated by SEM-EDS, XRD, AAS, UV–vis and 1-butene isomerization as a test reaction. Additionally, ash collected from the catalysts was characterized. The obtained results showed a decrease in the activity by ash and alkali metals originating from biomass. Neither the structural changes in the support nor the changes in the oxidation state and distribution of vanadium were observed during the entire testing period. The acidity of the catalyst, operated for the shortest period (2270h), increased due to the formation of sulfate species arising from the presence of SO₂ in the flue gases. The role of sulfate species and alkali cations in poisoning of catalytic sites is discussed.

Cet article expose les résultats d’une étude portant sur l’influence de l’empoisonnement du catalyseur de la RCS sur sa structure. Trois échantillons d’un catalyseur commercial de SCR ont été exposés aux gaz en sortie de brûleur dans une chaudière PF pendant la co-combustion de charbon et de biomasse. Les méthodes d’analyse utilisées sont le MEB-EDS, la DRX, la spectroscopie d’absorption atomique, la spectrométrie UV–vis et le test de réaction à l’isomérisation du 1-butène. Les cendres récupérées sur le catalyseur ont été caractérisés. L’activité diminue en présence de cendres et de métaux alcalins dans la biomasse. Ni la structure du support, ni l’état d’oxydation, ni la distribution du vanadium n’ont été modifiés durant toute la durée du test. L’acidité du catalyseur testé le moins longtemps (2270h) a augmenté du fait de la formation de dérivés du sulfate provenant du SO₂ contenu dans les gaz d’échappement. Le rôle de ces dérivés et des cations alcalins sur l’empoisonnement catalytique des sites est discuté.